2. Getting involved
3. Standards Committees
4. FNK

DIN Standards Committee Plastics

Overview

This International Standard specifies a method for the determination of the viscosity number of dilute solutions of polyamides in certain specified solvents. Polyamide samples must be completely soluble in the solvents mentioned. Additives such as flame-retardants and modifiers often interfere with the viscosity measurement, having an increasing effect on the viscosity number in formic acid and a decreasing effect on the viscosity number in sulfuric acid. The extent of the effect for polyamide compounds depends on the additive, the quantity of the additive, the presence of other additives and the compounding conditions. For pure polyamides or polyamides containing additives that do not interfere with the viscosity measurement, the determination of the viscosity number of a polyamide provides a measure of the molecular mass of the polymer. The viscosity number of pure polyamides or polyamides which contain additives that do not interfere with the viscosity measurement can be converted from one solvent to another. The viscosity number of polyamides containing additives that do interfere with the viscosity measurement is specific to the solvent used and the material composition. In this case, the measured viscosity number cannot be converted from one solvent to another. The method is applicable to the polyamides designated PA 46, PA 6, PA 66, PA 69, PA 610, PA 612, PA 11, PA 12, PA 6T/66, PA 6I/6T, PA 6T/6I/66, PA 6T/6I, PA 6I/6T/66 and PA MXD6 as defined in ISO 1874-1, as well as to copolyamides, compounds of polyamides and other polyamides that are soluble in one of the specified solvents under the specified conditions. The method is not applicable to polyamides produced by anionic polymerization of lactams or produced with cross-linking agents; such polyamides are normally insoluble in the specified solvents. The viscosity number is determined by the general procedure specified in ISO 1628-1, observing the particular conditions specified in this International Standard. This standard includes Amendment A1 approved by CEN on 02 April 2013. The following modifications have been made with respect to DIN EN ISO 307:2007-08: a) in clause 2 "Normative references" the reference to JIS K 6920-2:2000 has been omitted and transferred to the Bibliography; b) in 5.1.7, the density of the orthophosphoric acid has been changed to g/ml; c) in 10.2.2, 10.2.3 and 10.2.4 the first sentence "Weigh, to the nearest 0,2 mg, a test portion of (mc ± 5) mg" has been replaced by "Weigh, to the nearest 0,2 mg, a test portion of mass mt, where mt lies in the range (mc ± 5) mg"; d) in clause 11 "Expression of results" Equation (6), mc has been replaced by mt and in the definitions of the symbols used in the equations "mc" has been replaced by "mt is the mass of the test portion taken in 10.2.2, 10.2.3 or 10.2.4, in milligrams"; e) the title of Figure B.1 "Example of flow time/viscosity relationship" has been corrected to read "Example of flow time/concentration relationship"; f) in Table D.1, heading and first line, the unit of density "kg/m3" has been replaced by "kg/dm3"; g) throughout the document, "JIS K 6920-2:2000, Annex B" has been replaced by "JIS K 6920-2:2009, Annex JA"; h) the Bibliography in the National Annex NA (informative) has been updated. This International Standard ISO 307:2007 has been prepared in ISO/TC 61/SC 9 "Thermoplastic materials" (secretariat: KATS, Korea). CEN/TC 249 "Plastics", the secretariat of which is held by NBN, is responsible for the European Standard. On the national level the committee responsible for this standard is NA 054-02-10 AA "Thermoplast-Formmassen" ("Thermoplastic materials") at DIN.

Document: references other documents

Responsible national committee

NA 054-02-10 AA - Thermoplastic materials  

Responsible european committee

CEN/TC 249 - Plastics